In the silicone rubber manufacturing industry, IOTA 208 Methylphenyl Vinyl Silicone Resin has become the ideal material for warm liquid compression molding silicone rubber due to its outstanding Si-Vi reactivity and chemical stability. This resin not only significantly improves the molding efficiency of silicone rubber but also enhances its high-temperature resistance and chemical durability, providing an innovative solution for the silicone rubber industry.

Product Highlights:

• Superior Si-Vi Reactivity: Easily reacts with hydrogen-containing compounds, ensuring high curing efficiency.
• High-Temperature Resistance: Provides strong resistance to warm liquid compression molding, ensuring material stability at elevated temperatures.
• Low Reaction Temperature: Facilitates low-temperature addition reactions, requiring minimal catalyst use, ensuring complete reaction with a colorless and odorless finish.

Application Areas:

IOTA 208 is widely used in warm liquid compression molding silicone rubber, particularly in industrial applications requiring efficient molding and high-temperature durability.

Technical Specifications:

• Appearance: Colorless to transparent liquid
• Viscosity (25°C): 38,000-53,000 mPa·s
• Vinyl Content: 3.0-3.4%
• Curing Content: ≥96%

Packaging & Storage:

• Packaging: Polyethylene plastic drums in 5kg, 50kg, and 200kg sizes
• Storage: Keep in a cool, dry, and shaded place
• Shelf Life: 6 months

The introduction of IOTA 208 Methylphenyl Vinyl Silicone Resin provides the silicone rubber manufacturing industry with an efficient and stable solution, with great potential for expanding into more high-temperature and chemically stable applications in the future.