Innovative Application Directions:

1. Composite Interface Modifier:

   • Enhances resin-glass/metal interfacial bonding via Si-NH-Si reaction with substrate -OH groups

   • Only 0.5-2% addition significantly improves interlaminar shear strength

2. Functional Composite Preparation:

   • Compatible with epoxy silicone resins (30% faster curing)

   • Imparts hydrophobicity and corrosion resistance

   • Maintains composite transparency (>95% light transmittance)

Verified Technical Indicators:

• Cured hardness: 6H after 24h at room temperature

• Chemical stability: Resistant to O₂, H₂O permeation

• Process flexibility: Adjustable curing temperature (60-200°C)

Safety Instructions:
※ Must be stored at 0-20°C in shaded environment
※ Wear protective equipment during handling; avoid open flames
※ Seal immediately after use with nitrogen protection

Note: All data comes from actual IOTA 9283 test reports with verified application cases. We provide technical consultation and sample trials - contact us for more test data.